Tuesday, March 28, 2017

Magnesium and Its Alloys - Increasing Use in Products




Magnesium (Mg)  is  an  alkaline  earth  metal  having  atomic  number 12  with oxidation  number +2.

Density at 20°C (g/cm3) Magnesum 1.74 Aluminium  2.70 Iron 7.86


The cost of magnesium has been decreasing below the cost of the  aluminium since 2004. M
agnesium  melting  cost  is  2/3  compared  to  aluminium. In terms of productivity, magnesium provides    25%  higher  casting  productivity  compared  to  aluminium  pressure  die  casting,  300-  500% compared  to  aluminium  permanent  mold  casting,  and  200%  compared  to  polymer  injection molding.

Magnesium is considered to be a good choice material in the areas of defense and aerospace engineering for aircraft and missile components,  aircraft engine mounts,  control  hinges,  fuel  tanks,  wings.  In  automotive  sector  magnesium  is  used  for  wheels, housings, transmission cases, engine blocks, steering wheels and columns, seat  frames,  electronic goods  like  laptops,  televisions,  cell  phones  and  in  many  more  areas  (http://www.intlmag.org/).



ASTM  (American Society for Testing and Materials)  names the Magnesium alloys with two letters
defining  the  elements,  with  numbers  denoting  the  percentage  and  an  additional  digit  to indicate intermediate properties.


An ASTM code for magnesium’s alloying elements

Letter  Alloying Element     Letter  Alloying Element
A  Aluminum                      L  Lithium
B  Bismuth                         M  Manganese
C  Copper                           N  Nickel
D  Cadmium                       P  Lead
E  Rare Earths                    Q  Silver
F  Iron                                 R  Chromium
H  Thorium                         S  Silicon
Z  Zinc

For example, AZ 91 Mg alloy contain  aluminum  (Al) and  zinc (Zn) in 9%, 1% respectively in total and the rest by pure magnesium.

Source:
Magnesium and Its Alloys in Automotive Applications – A Review
D. Sameer Kumar, C. Tara Sasanka, K. Ravindra, K.N.S. Suman
American Journal of Materials Science and Technology
(2015) Vol. 4 No. 1 pp. 12-30


2017

Interviewed engineering graduates for four days during 28 to 31 March 2017. They do not know the usage of magnesium in mechanical engineering product components.


2016

Global demand for magnesium metal will reach 1,085 KT in 2016, representing market value worth US$ 3.13 Bn.
Magnesium’s applications in making automotive wheels, transmission cases, and engine blocks will continue to fuel demand in 2016 and beyond.
Application-wise, magnesium alloys and die-casting will continue to remain the largest segments, accounting for 349 KT and 302 KT respectively in 2016.
Magnesium will continue to witness stable demand from the aerospace sector, owing to its excellent properties as a reductant in manufacturing titanium.
The global magnesium metal market is anticipated to increase at a CAGR of 7.1% during 2016-2026, reaching 6.2 Bn in revenues by 2026.
http://www.futuremarketinsights.com/press-release/magnesium-metal-market

The automotive and transportation industries is one of the largest end-users for magnesium die-cast components such as assemblies, housings, and brackets. Average use of magnesium per vehicle is about two to three kilograms which could also go as high as 26 kilograms for some vehicles.
http://www.foundry-planet.com/equipment/detail-view/with-increasing-demand-from-auto-sector-global-magnesium-market-to-grow-by-573-by-2020/




Magnesium Alloys: The Future for Automotive Lightweighting?
Experts gathered at the University of Waterloo discussed the challenges and opportunities ultralightweight alloys pose
http://www.canadianmetalworking.com/article/metalworking/magnesium-alloys-future-automotive-lightweighting

2015
Magnesium Prices
http://www.metal-pages.com/metalprices/mangnesium/

2014



2013


Magnesium alloys are very attractive for a range of weight-sensitive applications. They have the largest strength-to-weight ratio of the common structural metals, are lighter than aluminum and are particularly favored for being easy to machine and for their ability to be die cast to net shape. Unfortunately, magnesium alloys tend to corrode too easily. A team at Monash University in Australia has now discovered a novel and potentially game-changing approach to the problem: poisoning the chemical reactions leading to corrosion of magnesium alloys by adding a dash of arsenic to the recipe.

Magnesium alloys are of great interest as lightweight replacements for aluminum, titanium, and steel components in a range of transportation and aerospace applications. However, magnesium alloys corrode easily, and this often prevents their use as substitute for noncorroding metals.  As a result, the use of magnesium alloys at present is less than a million tons per year, while nearly 50 million tons of aluminum alloys are used each year. The experimental demonstration of reduction in corrosion of magnesium is a welcome step.  The result was that addition of about one-third of a percent of arsenic to the magnesium alloy reduced its corrosion rate in a salt solution by a factor of nearly ten. In this initial study the intent was to prove the principle of the use of cathodic poisoning to reduce corrosion of Magnesium.

http://www.gizmag.com/stainless-magnesium-corrosion-monash/28856/


Updated 1 April 2017, 14 January 2015